Super fast curing adhesive with exceptional final bond strength. Based on SMX Polymer Technology, Turbo has rapid strength build-up after 20 minutes. Final bond strength achieved in 3 hours. For all types of bonding applications, onto all types of surfaces, even wet or humid non-porous surfaces. For all bonding applications where adhesive strength build up speed is highly critical or important. Heavy duty bonding in all weather conditions, on most surfaces. Suitable for bonding porous (i.e. natural stone) and non porous surfaces.
| Basis SMX Hybrid Polymer | |
| Consistency Stable paste | |
| Curing system Moisture curing | |
| Skin formation (23 Degrees C/50 Percent R.H.) Ca. 5 min | |
| Curing speed (23 Degrees C/50Percent R.H.) 2 mm/24h TO 3 mm/24h | |
| Hardness 65 � 5 Shore A | |
| Density 1,52 g/ml | |
| Elastic recovery (ISO 7389) > 75 Percent | |
| Maximum allowed distortion � 20 Percent | |
| Max. tension (ISO 37)** 3,80 N/mm� | |
| Elasticity modulus 100% (ISO 37)** 3,00 N/mm� | |
| Elongation at break (ISO 37)** 200 % | |
| Adjustable until Ca. 5 min | |
| Temperature resistance** -40 Degrees C TO 90 Degress C | |
| Application temperature 5 Degrees C TO 35 Degrees C | |